Abstract

The waste heat boiler in a sulfur-burning sulfuric acid plant experienced failures, specifically furnace tube bursting and tube sheet leakage. Samples were extracted from the front tube sheet and the tubes that had failed, located where the waste heat boiler had developed leaks. The compositions, microstructures, mechanical properties, and crack morphology of the tube sheet and the tubes were analyzed. There were many small cracks in the tube-sheet joints, and Na was detected in the cracks. Na was also found in the expanded connection area between the tubes and the tube sheet. The inner wall of the tubes near the tube burst area was severely corroded. The amount of S on the inner walls of the tubes near the tube burst area was significantly higher than that on the outer walls of the tubes. Through relevant analyses, the following conclusions were obtained: the alkali stress corrosion cracks widely appeared in the tube-sheet joint. The sulfuric acid formed by the mixture of leaked water and high-temperature flue gas flowed into the tubes, and relevant tubes were seriously corroded and eventually burst.

References

1.
Sui
,
R.
,
Wang
,
W.
,
Liu
,
Y.
,
Li
,
D.
, and
Li
,
W.
,
2014
, “
Root Cause Analysis of Stress Corrosion at Tube-to-Tubesheet Joints of a Waste Heat Boiler
,”
Eng. Failure Anal.
,
45
, pp.
398
405
.10.1016/j.engfailanal.2014.07.013
2.
Ding
,
Q.
,
Tang
,
X. F.
, and
Yang
,
Z. G.
,
2017
, “
Failure Analysis on Abnormal Corrosion of Economizer Tubes in a Waste Heat Boiler
,”
Eng. Failure Anal.
,
73
, pp.
129
138
.10.1016/j.engfailanal.2016.12.011
3.
Ebara
,
R.
,
Tanaka
,
F.
, and
Kawasaki
,
M.
,
2013
, “
Sulfuric Acid Dew Point Corrosion in Waste Heat Boiler Tube for Copper Smelting Furnace
,”
Eng. Failure Anal.
,
33
, pp.
29
36
.10.1016/j.engfailanal.2013.04.007
4.
Hu
,
Y.
,
Liu
,
J. J.
,
Li
,
F. Q.
, Liu, C. F., Wang, Y. J., and Han, J. P.,
2018
, “
Failure Analysis of Frequent Explosion of Waste Heat Boiler in Process of Methanol From Coal
,”
China Spec. Equip. Saf.
,
34
(
9
), pp.
69
73
.
5.
Xin
,
Y. C.
,
Shi
,
J.
,
Liu
,
W.
, and Du, C. Y.,
2019
, “
Failure Analysis for the Leakage on a Gastube Boiler in Service
,”
Heat Treat. Met.
,
44
, pp.
308
311
.
6.
Zhao
,
Y. L.
,
2020
, “
Cause Analysis on Cracking of Stainless Steel Flue Gas Pipe of Waste Heat Boile
,”
Phys. Test. Chem. Anal.
,
56
, pp.
34
37
.
7.
Lv
,
Q. H.
,
Ma
,
J. W.
,
Chen
,
S. F.
, Zhang, X. N., Ma, Y. M., Zhao, M. M., and Mei, G. X.,
2021
, “
Failure Analysis and Protective Measures of Boiler Tubes of an Exhaust Gas Waste-Heat Boiler in a Sulfur Recovery Unit
,”
Petro-Chem. Equip.
,
50
, pp.
68
71
.
8.
Sui
,
R. J.
,
Zhao
,
Y. L.
,
Ge
,
B. R.
, and
Wang
,
W. Q.
,
2021
, “
Failure Analysis of Leakage at Tube-to-Tube Sheet Joints of a Waste Heat Boiler
,”
Eng. Failure Anal.
,
129
, p.
105639
.10.1016/j.engfailanal.2021.105639
9.
Xu
,
S.
,
Wang
,
C.
, and
Wang
,
W.
,
2015
, “
Failure Analysis of Stress Corrosion Cracking in Heat Exchanger Tubes During Start-Up Operation
,”
Eng. Failure Anal.
,
51
, pp.
1
8
.10.1016/j.engfailanal.2015.02.005
10.
Xu
,
S.
, and
Wang
,
W.
,
2013
, “
Numerical Investigation on Weld Residual Stresses in Tube to Tube Sheet Joint of a Heat Exchanger
,”
Int. J. Pressure Vessels Piping
,
101
, pp.
37
44
.10.1016/j.ijpvp.2012.10.004
11.
Xu
,
S.
, and
Zhao
,
Y.
,
2013
, “
Using FEM to Determine the Thermo-Mechanical Stress in Tube to Tube–Sheet Joint for the SCC Failure Analysis
,”
Eng. Failure Anal.
,
34
, pp.
24
34
.10.1016/j.engfailanal.2013.07.011
12.
Azevedo
,
C. R. F.
,
Beneduce
,
N.
,
Brandi
,
S.
, and
Tschiptschin
,
A.
,
2008
, “
Cracking of 2.25Cr–1.0Mo Steel Tube/Stationary Tubesheet Weldment of a Heat-Exchanger
,”
Eng. Failure Anal.
,
15
(
6
), pp.
695
710
.10.1016/j.engfailanal.2007.06.013
13.
Chinese Standard, GB/T 713-2014
, “
Steel Plates for Boilers and Pressure Vessels, China, [S]
,” China Iron & Steel Association, Beijing, China.
14.
Chinese Standard, GB/T 9948-2013
, “
Seamless Steel Pipe for Petroleum Cracking, China, [S]
,” China Iron & Steel Association, Beijing, China.
15.
Chinese Standard, GB/T 13299-1991
, “
Method for Evaluating the Microstructure of Steel, China, [S]
,” China Iron & Steel Association, Beijing, China.
You do not currently have access to this content.