Despite the many advantages of using lasers for welding ceramics (alumina in particular), cracks induced by the resulting and severe thermal stresses are often detrimental to weld quality and strength. While many factors contribute to the formation of these cracks, it is the inevitable and localized increase in temperature and the ensuing thermal stresses that usually cause the damage. To help avoid the use of a separate preheating step, while at the same time allowing for faster joining, a unique method of dual-beam laser welding was developed and qualitatively assessed. The approach outlined in this paper utilizes two beams split from a single, 500 W (1.5 kW peak) system to more gradually introduce the energy required to melt and bond alumina. The first or lead beam raises the local temperature just below the melting point, while the second beam introduces additional heat sufficient to melt and bond the samples. Using feed rates of 5.1 mm/s and beam separation distances ranging from 0.5 mm to 2.3 mm, clean and relatively straight weld geometries were observed at total power levels of approximately . Relatively straight and uniform welds with considerable dross occurred at smaller beam separations and higher power levels. Uneven weld lines sans discernible cracks were observed at power levels below 206 W. Based on these preliminary observations, the two-beam approach was qualitatively shown to be capable of influencing and, in some instances, improving weld characteristics in terms of overall quality, dross, and crack formation.
Skip Nav Destination
e-mail: aesegall@psu.edu
Article navigation
February 2011
Research Papers
Welding of Alumina Using a Pulsed Dual-Beam Laser
J. Harris,
J. Harris
Engineering Science and Mechanics,
Pennsylvania State University
, University Park, PA 16802
Search for other works by this author on:
R. Akarapu,
R. Akarapu
Engineering Science and Mechanics,
Pennsylvania State University
, University Park, PA 16802
Search for other works by this author on:
A. E. Segall
A. E. Segall
Engineering Science and Mechanics,
e-mail: aesegall@psu.edu
Pennsylvania State University
, University Park, PA 16802
Search for other works by this author on:
J. Harris
Engineering Science and Mechanics,
Pennsylvania State University
, University Park, PA 16802
R. Akarapu
Engineering Science and Mechanics,
Pennsylvania State University
, University Park, PA 16802
A. E. Segall
Engineering Science and Mechanics,
Pennsylvania State University
, University Park, PA 16802e-mail: aesegall@psu.edu
J. Manuf. Sci. Eng. Feb 2011, 133(1): 011001 (6 pages)
Published Online: January 5, 2011
Article history
Received:
April 17, 2009
Revised:
November 12, 2010
Online:
January 5, 2011
Published:
January 5, 2011
Citation
Harris, J., Akarapu, R., and Segall, A. E. (January 5, 2011). "Welding of Alumina Using a Pulsed Dual-Beam Laser." ASME. J. Manuf. Sci. Eng. February 2011; 133(1): 011001. https://doi.org/10.1115/1.4003119
Download citation file:
Get Email Alerts
Cited By
Related Articles
Thermal Stresses Due to Laser Welding in Bridge-Wire Initiators
J. Electron. Packag (March,2009)
A Comparative Study of Formability of Diode Laser Welds in DP980 and HSLA Steels
J. Eng. Mater. Technol (July,2007)
Laser Transmission Welding of Thermoplastics—Part II: Experimental Model Validation
J. Manuf. Sci. Eng (October,2007)
Numerical Simulations and Experimental Results of Tensile Test Behavior of Laser Butt Welded DP980 Steels
J. Eng. Mater. Technol (October,2008)
Related Proceedings Papers
Related Chapters
Defining Joint Quality Using Weld Attributes
Ultrasonic Welding of Lithium-Ion Batteries
Introduction
Ultrasonic Welding of Lithium-Ion Batteries
Design Criteria for Thermal Stress
Process Piping: The Complete Guide to ASME B31.3, Third Edition