Friction stir welding (FSW) of electrolytic tough pitch copper plates was conducted using a conventional CNC milling machine. The microstructure evolution of the weld was correlated with the process parameters used in the study and in conjunction with increasing temperatures during processing. When the optimum process parameters were achieved, a sound weld joint was obtained. The weldments were evaluated by microstructural analysis, using optical and scanning electron microscopes, and in terms of mechanical properties. At early stages of FSW and/or when using less than optimum welding parameters low temperatures result, metal does not plasticize effectively producing defects, such as large cavities, porosity, and poor bonding, due to the lack of plasticized material. Cavities were found at the advancing region of the weld, and in this area the finest grains were observed from the entire weld. The cavities were reduced, and the grain size increased further along in the weld as the temperature increased also. The typical weld nugget found in the friction stir welding of other metals was not observed in this case. Dynamic recrystallization was observed in the “stirred zone” of the weld; considering that the strain rate in this region was the same in all three cases, the difference in grain size was attributed to the differences in process temperature.
Skip Nav Destination
e-mail: apolar@uic.edu
e-mail: jeindaco@uic.edu
Article navigation
June 2009
Research Papers
Microstructural Assessment of Copper Friction Stir Welds
A. Polar,
A. Polar
Department of Materials Engineering,
e-mail: apolar@uic.edu
University of Illinois at Chicago
, Chicago, IL 60607
Search for other works by this author on:
J. E. Indacochea
J. E. Indacochea
Department of Materials Engineering,
e-mail: jeindaco@uic.edu
University of Illinois at Chicago
, Chicago, IL 60607
Search for other works by this author on:
A. Polar
Department of Materials Engineering,
University of Illinois at Chicago
, Chicago, IL 60607e-mail: apolar@uic.edu
J. E. Indacochea
Department of Materials Engineering,
University of Illinois at Chicago
, Chicago, IL 60607e-mail: jeindaco@uic.edu
J. Manuf. Sci. Eng. Jun 2009, 131(3): 031012 (7 pages)
Published Online: May 20, 2009
Article history
Received:
February 2, 2006
Revised:
February 3, 2009
Published:
May 20, 2009
Citation
Polar, A., and Indacochea, J. E. (May 20, 2009). "Microstructural Assessment of Copper Friction Stir Welds." ASME. J. Manuf. Sci. Eng. June 2009; 131(3): 031012. https://doi.org/10.1115/1.3123313
Download citation file:
Get Email Alerts
Related Articles
Continuous Drive Friction Welding of AISI 8630 Low-Alloy Steel: Experimental Investigations on Microstructure Evolution and Mechanical Properties
J. Manuf. Sci. Eng (July,2022)
Optimization of a Weld Overlay on a Plate Structure
J. Pressure Vessel Technol (February,2010)
Metallurgical Phenomena Modeling in Friction Stir Welding of Aluminium Alloys: Analytical Versus Neural Network Based Approaches
J. Eng. Mater. Technol (July,2008)
The Effects of Filler Metal Transformation Temperature on Residual Stresses in a High Strength Steel Weld
J. Pressure Vessel Technol (August,2009)
Related Chapters
Defining Joint Quality Using Weld Attributes
Ultrasonic Welding of Lithium-Ion Batteries
The Relation between Cold-Work-Induced Microstructural Evolution and the Postannealing Grain Structures in Zircaloy-4
Zirconium in the Nuclear Industry: 20th International Symposium
Microstructure Evolution and Physics-Based Modeling
Ultrasonic Welding of Lithium-Ion Batteries