Hot section components in high-performance aircraft and rocket engines are increasingly being made of single crystal nickel superalloys such as PWA1480, PWA1484, CMSX-4, and Rene N-4 as these materials provide superior creep, stress rupture, melt resistance, and thermomechanical fatigue capabilities over their polycrystalline counterparts. Fatigue failures in PWA1480 single crystal nickel-base superalloy turbine blades used in the space shuttle main engine fuel turbopump are discussed. During testing many turbine blades experienced stage II noncrystallographic fatigue cracks with multiple origins at the core leading edge radius and extending down the airfoil span along the core surface. The longer cracks transitioned from stage II fatigue to crystallographic stage I fatigue propagation, on octahedral planes. An investigation of crack depths on the population of blades as a function of secondary crystallographic orientation (β) revealed that for β=45+/−15 deg tip cracks arrested after some growth or did not initiate at all. Finite element analysis of stress response at the blade tip, as a function of primary and secondary crystal orientation, revealed that there are preferential β orientations for which crack growth is minimized at the blade tip. To assess blade fatigue life and durability extensive testing of uniaxial single crystal specimens with different orientations has been tested over a wide temperature range in air and hydrogen. A detailed analysis of the experimentally determined low cycle fatigue properties for PWA1480 and SC 7-14-6 single crystal materials as a function of specimen crystallographic orientation is presented at high temperature (75°F–1800°F) in high-pressure hydrogen and air. Fatigue failure parameters are investigated for low cycle fatigue data of single crystal material based on the shear stress amplitudes on the 24 octahedral and 6 cube slip systems for FCC single crystals. The max shear stress amplitude on the slip planes reduces the scatter in the low cycle fatigue data and is found to be a good fatigue damage parameter, especially at elevated temperatures. The parameter did not characterize the room temperature low cycle fatigue data in high-pressure hydrogen well because of the noncrystallographic eutectic failure mechanism activated by hydrogen at room temperature. Fatigue life equations are developed for various temperature ranges and environmental conditions based on power-law curve fits of the failure parameter with low cycle fatigue test data. These curve fits can be used for assessing blade fatigue life.
Skip Nav Destination
Article navigation
July 2004
Technical Papers
High-Temperature Fatigue Properties of Single Crystal Superalloys in Air and Hydrogen
N. K. Arakere, Associate Professor,
N. K. Arakere, Associate Professor,
Mechanical Engineering Department, University of Florida, Gainesville, FL 32611-6300
Search for other works by this author on:
N. K. Arakere, Associate Professor,
Mechanical Engineering Department, University of Florida, Gainesville, FL 32611-6300
Contributed by the International Gas Turbine Institute (IGTI) of THE AMERICAN SOCIETY OF MECHANICAL ENGINEERS for publication in the ASME JOURNAL OF ENGINEERING FOR GAS TURBINES AND POWER. Paper presented at the International Gas Turbine and Aeroengine Congress and Exhibition, New Orleans, LA, June 4–7, 2001; Paper 01-GT-0585. Manuscript received by IGTI, December 2000; final revision, March 2001. Associate Editor: R. Natole.
J. Eng. Gas Turbines Power. Jul 2004, 126(3): 590-603 (14 pages)
Published Online: August 11, 2004
Article history
Received:
December 1, 2000
Revised:
March 1, 2001
Online:
August 11, 2004
Citation
Arakere, N. K. (August 11, 2004). "High-Temperature Fatigue Properties of Single Crystal Superalloys in Air and Hydrogen ." ASME. J. Eng. Gas Turbines Power. July 2004; 126(3): 590–603. https://doi.org/10.1115/1.1501075
Download citation file:
Get Email Alerts
Experimental Identification Of Blade Tip Rub Forces At Engine Relevant Temperatures And Speeds
J. Eng. Gas Turbines Power
Study Of Tandem Rotor Dual Wake Interaction With Downstream Stator Under Unsteady Numerical Approach
J. Eng. Gas Turbines Power
Experimental Design Validation of a Swirl-Stabilized Burner With Fluidically Variable Swirl Number
J. Eng. Gas Turbines Power (April 2025)
Experimental Characterization of a Bladeless Air Compressor
J. Eng. Gas Turbines Power (April 2025)
Related Articles
Effect of Crystal Orientation on Fatigue Failure of Single Crystal Nickel Base Turbine Blade Superalloys
J. Eng. Gas Turbines Power (January,2002)
Critical Plane Fatigue Modeling and Characterization of Single Crystal Nickel Superalloys
J. Eng. Gas Turbines Power (April,2004)
Fretting Stresses in Single Crystal Superalloy Turbine Blade Attachments
J. Tribol (April,2001)
Nonlocal Cyclic Life Prediction for Gas Turbine Components With
Sharply Notched Geometries
J. Eng. Gas Turbines Power (January,2008)
Related Proceedings Papers
Related Chapters
Crystal Orientation Optimization of Nickel-Based Single Crystal Turbine Blade
International Conference on Optimization Design (ICOD 2010)
Effects of Hydrogen Pressure on Crack Growth Rates in an Iron Based Superalloy
International Hydrogen Conference (IHC 2016): Materials Performance in Hydrogen Environments
Effect of Hydrogen on Corrosion of Zircaloy-4 under Irradiation
Zirconium in the Nuclear Industry: 20th International Symposium