Delamination cracking in thermal barrier coating (TBC) system is studied with the newly developed theoretical model. A semi-infinite long interface crack is pre-existing. The thermal stress and temperature gradient in TBC system are designated by a membrane stress P and a bending moment M. In this case, the effects of plastic deformation, creep of ceramic coating, as well as thermal growth oxidation and temperature gradient in TBC system are considered in the model due to the fact that these effects are considered in the calculation of thermal stress. The energy release rate, mode I and mode II stress intensity factors, as well as mode mixed measure ψ, are derived. The emphatic discussion about PSZ/Ni-alloy reveals that the TBC system may not fail in the form of coating delamination during the period of heat hold. However, the failure may be in the form of coating delamination during cooling or in the heating period during the second cycle or later cycles. The conclusion is consistent with the experimental observations. The delamination of ceramic coating is induced by the compressive load in the coating.
Skip Nav Destination
Article navigation
October 2002
Technical Papers
Delamination Cracking in Thermal Barrier Coating System
Y. C. Zhou,
Y. C. Zhou
Fracture Research Institute, Tohoku University, Sendai 980-8579, Japan
and Institute of Fundamental Mechanics and Materials Engineering, Xiangtan University, Xiangtan, Hunan 411105, P. R. China
Search for other works by this author on:
T. Hashida
T. Hashida
Fracture Research Institute, Tohoku University, Sendai 980-8579, Japan
Search for other works by this author on:
Y. C. Zhou
Fracture Research Institute, Tohoku University, Sendai 980-8579, Japan
and Institute of Fundamental Mechanics and Materials Engineering, Xiangtan University, Xiangtan, Hunan 411105, P. R. China
T. Hashida
Fracture Research Institute, Tohoku University, Sendai 980-8579, Japan
Contributed by the IGTI Technical Committee of THE AMERICAN SOCIETY OF MECHANICAL ENGINEERS for publication in the ASME JOURNAL OF ENGINEERING FOR GAS TURBINES AND POWER. Manuscript received by the IGTI Technical Committee July 2000; final revision received by the ASME Headquarters September 2001. Associate Editor: J. Conner.
J. Eng. Gas Turbines Power. Oct 2002, 124(4): 922-930 (9 pages)
Published Online: September 24, 2002
Article history
Received:
July 1, 2000
Revised:
September 1, 2001
Online:
September 24, 2002
Citation
Zhou, Y. C., and Hashida, T. (September 24, 2002). "Delamination Cracking in Thermal Barrier Coating System ." ASME. J. Eng. Gas Turbines Power. October 2002; 124(4): 922–930. https://doi.org/10.1115/1.1477194
Download citation file:
Get Email Alerts
Cited By
Heat Release Characteristics of a Volatile, Oxygenated, and Reactive Fuel in a Direct Injection Engine
J. Eng. Gas Turbines Power
Comprehensive Life Cycle Analysis of Diverse Hydrogen Production Routes and Application on a Hydrogen Engine
J. Eng. Gas Turbines Power
Related Articles
Effect of Time and Temperature on Thermal Barrier Coating Failure Mode Under Oxidizing Environment
J. Eng. Gas Turbines Power (March,2009)
Characterization of Fatigue Mechanisms of Thermal Barrier Coatings by a Novel Laser-Based Test
J. Eng. Gas Turbines Power (April,1999)
Mechanisms of Acute Angle Laser Drilling Induced Thermal Barrier Coating Delamination
J. Manuf. Sci. Eng (October,2009)
Deformation of Plasma Sprayed Thermal Barrier Coatings
J. Eng. Gas Turbines Power (July,2000)
Related Proceedings Papers
Related Chapters
Surface Analysis and Tools
Tribology of Mechanical Systems: A Guide to Present and Future Technologies
Radial Delayed Hydride Cracking in Irradiated Zircaloy-2 Cladding: Advanced Characterization Techniques
Zirconium in the Nuclear Industry: 20th International Symposium
Understanding the Problem
Design and Application of the Worm Gear