The use of high performance ceramic thermal barrier coatings in stationary gas turbines requires fundamental knowledge of their fatigue behavior under high temperature gradients and thermal cycling. An experimental method based on rapid laser heating complemented with finite-element calculations was developed in order to identify the major damage mechanisms and to obtain a data set for reliability assessment of thermal barrier coatings for temperature and stress fields similar to gas turbine conditions. The observed failures are strongly related to the pretreatment procedures such as annealing under high temperature gradients and isothermal long-term oxidation. The vertical crack patterns observed closed to the top surface of the Zirconia coating are generated at the moment of rapid cooling. These cracks are induced by high biaxial tensile stresses caused by the temperature gradient and the stress reversion after relaxation of compressive stresses at high temperatures. The long-term fatigue behavior is decisively determined by two processes: (1) the porous Zirconia loses its damage tolerant properties by densification, and (2) the growth of an oxide layer at the bond coat degrades adhesion and produces localized stress fields at the interface. Cyclic loads increase the length of existing in-plane cracks and delaminations rather than enlarging their number. Misfit of the crack flanks and wedge effects are the driving forces for continued crack propagation. These experimental results are discussed in terms of fracture mechanics.
Skip Nav Destination
Article navigation
April 1999
Research Papers
Characterization of Fatigue Mechanisms of Thermal Barrier Coatings by a Novel Laser-Based Test
U. Rettig,
U. Rettig
Siemes AG, ZT MF2, Otto-Hahn-Ring 6, Munich, Germany, 81739
Search for other works by this author on:
U. Bast,
U. Bast
Siemes AG, ZT MF2, Otto-Hahn-Ring 6, Munich, Germany, 81739
Search for other works by this author on:
D. Steiner,
D. Steiner
Siemes AG, ZT MF2, Otto-Hahn-Ring 6, Munich, Germany, 81739
Search for other works by this author on:
M. Oechsner
M. Oechsner
Siemes AG, ZT MF2, Otto-Hahn-Ring 6, Munich, Germany, 81739
Search for other works by this author on:
U. Rettig
Siemes AG, ZT MF2, Otto-Hahn-Ring 6, Munich, Germany, 81739
U. Bast
Siemes AG, ZT MF2, Otto-Hahn-Ring 6, Munich, Germany, 81739
D. Steiner
Siemes AG, ZT MF2, Otto-Hahn-Ring 6, Munich, Germany, 81739
M. Oechsner
Siemes AG, ZT MF2, Otto-Hahn-Ring 6, Munich, Germany, 81739
J. Eng. Gas Turbines Power. Apr 1999, 121(2): 259-264 (6 pages)
Published Online: April 1, 1999
Article history
Received:
April 1, 1998
Online:
December 3, 2007
Citation
Rettig, U., Bast, U., Steiner, D., and Oechsner, M. (April 1, 1999). "Characterization of Fatigue Mechanisms of Thermal Barrier Coatings by a Novel Laser-Based Test." ASME. J. Eng. Gas Turbines Power. April 1999; 121(2): 259–264. https://doi.org/10.1115/1.2817115
Download citation file:
Get Email Alerts
Cited By
Image-based flashback detection in a hydrogen-fired gas turbine using a convolutional autoencoder
J. Eng. Gas Turbines Power
Fuel Thermal Management and Injector Part Design for LPBF Manufacturing
J. Eng. Gas Turbines Power
An investigation of a multi-injector, premix/micromix burner burning pure methane to pure hydrogen
J. Eng. Gas Turbines Power
Related Articles
Assessing the Structural Integrity of Plasma-Sprayed Multilayer Thermal Barrier Coatings
J. Eng. Gas Turbines Power (March,2023)
Delamination Cracking in Thermal Barrier Coating System
J. Eng. Gas Turbines Power (October,2002)
The Creep Damage Behavior of the Plasma-Sprayed Thermal Barrier Coating System NiCr22Co12Mo9-NiCoCrAlY-ZrO 2 /7%Y 2 O 3
J. Eng. Gas Turbines Power (October,1999)
Effect of Time and Temperature on Thermal Barrier Coating Failure Mode Under Oxidizing Environment
J. Eng. Gas Turbines Power (March,2009)
Related Chapters
Surface Analysis and Tools
Tribology of Mechanical Systems: A Guide to Present and Future Technologies
Fatigue Analysis in the Connecting Rod of MF285 Tractor by Finite Element Method
International Conference on Advanced Computer Theory and Engineering, 4th (ICACTE 2011)
Understanding the Problem
Design and Application of the Worm Gear