The failure probability of notched tensile bars is calculated using the multi-axial Weibull theory. The influence exerted by the stress concentration factor, the stress gradient in the notch root, and the Weibull exponent is analyzed.
Issue Section:
Gas Turbines: Ceramics
1.
Peterson, R. E., Stress Concentration Factors, Wiley, New York, 1974.
2.
Batdorf
S. B.
Crose
J. G.
A Statistical Theory for the Fracture of Brittle Structures Subjected to Nonuniform Stress
,” ASME Journal of Applied Mechanics
, Vol. 41
, 1974
, pp. 459
–461
.3.
Batdorf
S. B.
Heinisch
H. L.
Weakest Link Theory Reformulated for Arbitrary Fracture Criterion
,” J. Amer. Ceram. Soc.
, Vol. 61
, 1978
, pp. 355
–358
.4.
Evans
A. G.
A General Approach for the Statistical Analysis of Multiaxial Fracture
,” J. Am. Ceram. Soc.
, Vol. 61
, 1978
, pp. 302
–308
.5.
Matsuo
Y.
A Probabilistic Analysis of Fracture Loci Under Bi-axial Stress State
,” Bull. JSME
, Vol. 24
, 1981
, pp. 290
–294
.6.
Thiemeier
T.
Bru¨ckner-Foit
A.
Ko¨lker
H.
Influence of the Fracture Criterion on the Failure Probability of Ceramic Components
,” J. Am. Ceram. Soc.
, Vol. 74
, 1991
, pp. 48
–52
.7.
Paris, P. C., and Sih, G. C., “Stress Analysis of Cracks,” in: Fracture Toughness Testing and Its Applications, ASTM STP 381, American Society of Testing of Materials, Philadelphia, PA, 1965, pp. 30–83.
8.
Heger, A., Bru¨ckner-Foit, A., and Munz, D., “STAU—ein Programm zur Berechnung der Ausfallwahrscheinlichkeiten mehrachsig beanspruchter keramischer Komponenten als Post-Prozessor fu¨r Finite-Elemente-Programme,” Internal Report, Institute for Reliability and Failure Analysis, University of Karlsruhe, Germany, 1991.
9.
Nemeth, N. N., Manderscheid, J. M., and Gyekenyesi, J. P., “Ceramic Analysis and Reliability Evaluation of Structures (CARES),” User’s and Programmer’s Manual, NASA TP-2916, Washington, DC, 1989.
This content is only available via PDF.
Copyright © 1995
by The American Society of Mechanical Engineers
You do not currently have access to this content.